TYPICAL PROPERTIES (1) | |||
MECHANICAL机械性能 | Value | Unit | Standard |
Tensile Stress, yld, Type I, 50 mm/min / 抗拉强度,屈服,类型I,50 mm/min | 77 | MPa | ASTM D 638 |
Tensile Stress, brk, Type I, 50 mm/min / 抗拉强度, 断裂, 类型I, 50 mm/min | 64 | MPa | ASTM D 638 |
Tensile Strain, yld, Type I, 50 mm/min / 拉伸伸长, 屈服, 类型I, 50 mm/min | 7 | % | ASTM D 638 |
Tensile Strain, brk, Type I, 50 mm/min / 拉伸伸长,断裂,类型I, 50 mm/min | 92 | % | ASTM D 638 |
Tensile Modulus, 50 mm/min / 拉伸模量,50 mm/min | 2830 | MPa | ASTM D 638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span / 挠曲强度, 屈服, 1.3 mm/min, 50 mm 跨距 | 116 | MPa | ASTM D 790 |
Flexural Modulus, 1.3 mm/min, 50 mm span / 挠曲模量, 1.3 mm/min, 50 mm 跨距 | 2630 | MPa | ASTM D 790 |
Tensile Stress, yield 50 mm/min / 抗张程度,屈服, 50 mm/min | 77 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min / 抗张程度,断裂,50mm/min | 62 | MPa | ISO 527 |
Tensile Strain, yield, 50 mm/min / 拉伸伸长,屈服,,50mm/min | 8 | % | ISO 527 |
Tensile Strain, break, 50 mm/min / 拉伸伸长,断裂,50mm/min | 60 | % | ISO 527 |
Tensile Modulus, 1 mm/min / 拉伸模量,1 mm/min | 2400 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min / 弯曲强度,屈服,2 mm/min | 101 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min / 弯曲模量,2 mm/min | 2310 | MPa | ISO 178 |
Pencil Hardness test, 1kgf | F | – | ASTM D 3363 |
Erichson scratch depth, 6N | 14 | micrometer | SABIC Method |
IMPACT | Value | Unit | Standard |
Izod Impact, unnotched, 23°C / 无缺口悬臂梁冲击 23°C | NB | J/m | ASTM D 4812 |
Izod Impact, notched, 23°C / 悬臂梁缺口冲击强度23°C | 37 | J/m | ASTM D 256 |
Izod IMPACT, notched, -30°C / 悬壁梁缺口冲击强度, -30°C | 32 | J/m | ASTM D 256 |
Instrumented Impact Total Energy, 23°C / 仪表控制抗冲击总能量,23°C | 68 | J | ASTM D 3763 |
Izod IMPACT, unnotched 80*10*3 +23°C | NB | kJ/m² | ISO 180/1U |
Izod IMPACT, unnotched 80*10*3 -30°C | 93 | kJ/m² | ISO 180/1U |
Izod IMPACT, notched 80*10*3 +23°C / 悬壁梁缺口冲击强度, 80*10*3 +23°C | 6 | kJ/m² | ISO 180/1A |
Izod IMPACT, notched 80*10*3 -30°C / 悬壁梁缺口冲击强度, 80*10*3 -30°C | 4 | kJ/m² | ISO 180/1A |
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm / 简支梁缺口冲击强度,23°C,C80*10*3 sp=62mm | 3 | kJ/m² | ISO 179/1eA |
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm / 简支梁缺口冲击强度,-30°C,C80*10*3 sp=62mm | 3 | kJ/m² | ISO 179/1eA |
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | 133 | kJ/m² | ISO 179/1eU |
THERMAL | Value | Unit | Standard |
Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50 | 138 | °C | ASTM D 1525 |
HDT, 0.45 MPa, 3.2 mm, unannealed / 热变形温度,0.45 MPa, 3.2 mm,未退火 | 133 | °C | ASTM D 648 |
HDT, 1.82 MPa, 3.2mm, unannealed / 热变形温度,1.82 MPa, 3.2mm,未退火 | 121 | °C | ASTM D 648 |
CTE, -40°C to 95°C, flow / 热膨胀系数,-40°C 到 95°C, 流动 | 6.E-05 | 1/°C | ASTM E 831 |
CTE, -40°C to 95°C, xflow | 6.E-05 | 1/°C | ASTM E 831 |
CTE, 23°C to 80°C, flow | 6.E-05 | 1/°C | ISO 11359-2 |
CTE, 23°C to 80°C, xflow | 6.E-05 | 1/°C | ISO 11359-2 |
Ball Pressure Test, 125°C +/- 2°C | Pass | – | IEC 60695-10-2 |
Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50 | 141 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 / 维卡软化温度,B级/120 | 142 | °C | ISO 306 |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 134 | °C | ISO 75/Bf |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm / 热变形温度,1.8 MPa, 未退火,80*10*4, 64.0 mm 跨距 | 121 | °C | ISO 75/Af |
PHYSICAL | Value | Unit | Standard |
Specific Gravity/比重 | 1.18 | – | ASTM D 792 |
Specific Volume/比容 | 0.85 | cm³/g | ASTM D 792 |
Density/密度 | 1.17 | g/cm³ | ASTM D 792 |
Water Absorption, 24 hours / 吸水率, 24小时 | 0.1 | % | ASTM D 570 |
Water Absorption, equilibrium, 23C / 吸水率,平衡,23C | 0.3 | % | ASTM D 570 |
Water Absorption, 50% RH, equilib | 0.14 | % | ASTM D 570 |
Moisture Absorption, 50% RH, 24 hrs | 0.05 | % | ASTM D 570 |
Mold Shrinkage, flow, 3.2 mm / 模塑收缩量,流动,3.2 mm | 0.5 – 0.8 | % | SABIC Method |
Melt Flow Rate / 熔流率, 300°C/1.2 kgf / 熔流率,300°C/1.2 kgf | 17.1 | g/10 min | ASTM D 1238 |
Density/密度 | 1.17 | g/cm³ | ISO 1183 |
Water Absorption, (23°C/sat) / 吸水率, (23°C/sat) | 0.3 | % | ISO 62 |
Moisture Absorption (23°C / 50% RH) / 吸水率, 平衡,(23°C / 50% RH) | 0.14 | % | ISO 62 |
Melt Volume Rate, MVR at 300°C/1.2 kg | 16 | cm³/10 min | ISO 1133 |
OPTICAL | Value | Unit | Standard |
Light Transmission/透光率 | 88 | % | ASTM D 1003 |
Haze/雾度 | <0.8 | % | ASTM D 1003 |
Refractive Index /折射指数 | 1.584 | – | ASTM D 542 |
Refractive Index /折射指数 | 1.584 | – | ISO 489 |
FLAME CHARACTERISTICS | Value | Unit | Standard |
UL Recognized, 94HB Flame Class Rating (3) / UL认可,94HB 阻燃等级(3) | 0.75 | mm | UL 94 |
Source GMD, last updated:03/27/2007 |
Processing |
Parameter | ||
Injection Molding | Value | Unit |
Drying Temperature / 干燥温度 | 120 | °C |
Drying Time / 干燥时间 | 3 – 4 | hrs |
Maximum Moisture Content / 最大含湿量 | 0.02 | % |
Melt Temperature / 熔体温度 | 295 – 315 | °C |
Nozzle Temperature / 注嘴温度 | 290 – 310 | °C |
Front – Zone 3 Temperature / 前区3温度 | 295 – 315 | °C |
Middle – Zone 2 Temperature / 中区2温度 | 280 – 305 | °C |
Rear – Zone 1 Temperature / 后区1温度 | 260 – 280 | °C |
Hopper Temperature / 料筒温度 | 60 – 80 | °C |
Mold Temperature / 模具温度 | 70 – 95 | °C |
本文标签: PPS塑胶原料,PEEK塑胶原料,PPA尼龙料,PA66塑胶原料,POM塑胶原料,PPSU塑胶原料,PSU塑胶原料,TPU塑胶原料供应商